Slag Pot, Slag Ladle, Casting Part manufacturer / supplier in China, offering Citic Useful Foundry Ladle Casting Steel Slag Pot for Steel Plant, Citicic Professional Steam Calcination Rotary Kiln with Best Price, Professional Wet Procces Cement Rotary Kiln and so on.

(/ )

Supplier Homepage Product Metallurgy & Chemical Rotary Furnace&Slag Pot Citic Useful Foundry Ladle Casting Steel Slag Pot for Steel Plant

Citic Useful Foundry Ladle Casting Steel Slag Pot for Steel Plant

FOB Price: US $20,000 / Piece
Min. Order: 1 Piece
Min. Order FOB Price
1 Piece US $20,000/ Piece
Get Latest Price
Production Capacity: 2000PCS/Year
Transport Package: Slag Pots in Cast Steel & Slag Ladle
Payment Terms: L/C, T/T

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Casting Method: Special Casting
  • Casting Metal: Cast Steel
  • Surface Treatment: Polishing
  • Coating: Sodium silicate
  • Standard: AISI
  • Slag Pots in Cast Steel: Heavy Fabrication Division
  • Fact Cubage: 22 Cbm
  • Product Application: Slag Pot in Steel Works.
  • Quality System: ISO 9001
  • Quality Inspection: Chemical Analysis; -Mechanical Performance; -Dim
  • Trademark: CITICIC
  • Origin: Luoyang, Henan
  • Casting Form Material: Steel
  • Casting Form Usage Count: Permanent
  • Surface Roughness: Ra3.2
  • Machining Tolerance: +/-0.01mm
  • Certification: CE, ISO 9001:2000
  • Materia: DIN 17182 GS-16mn5 1.1131
  • Weight: 10 -100 T
  • Cast Tolerance: Unless Otherwise ASTM, En, DIN, ISO, JIS, GB
  • Pattern: New Natural Wooden Mold;
  • Name: Slag Pot
  • Specification: Slag Pots in Cast Steel & Slag Ladle
Product Description

Casting Slag Pot
Heavy Fabrication Division
Slag Pots in Cast Steel 
expertise products made in China
Specifications
-Accurate dimension; 
-ISO 9001 quality system; 
-Safe operating product; 
-Professional casting skill; 
-Complete requirements
Casting Slag Pot(metallurgy slag pot)
 

Feature:
Material: steel, self-smelting according to standard: ASTM, EN, DIN,ISO, JIS, GB, etc;
Sand mold casting: Steel casting, through sodium silicated-bonded sand and/or resin sand;
Pattern: new natural wooden mold;
Non-destructive examination:
-visual detection ;
-Ultrasonic test ;
-Magnetic particle inspection ;
Quality inspection:
-Chemical analysis;
-Mechanical performance;
-Dimension report;
Cast Tolerance: unless otherwise  ASTM, EN, DIN,ISO, JIS, GB
Machining tolerance: unless otherwise according to dwg. requirement;
 
Product Parameter:
Material: DIN 17182 GS-16Mn5 1.1131
Fact cubage: 22 CBM 
Appro.Net Wt.: 10 -100 t 
Product application: slag pot in steel works.
 is a modern industrial China group specialized in the producing of heavy plates 
in low-alloyed carbon steel grades. Organised as full integrated works, the major production facilities 
include cokery plant, blast-furnaces, oxygen steelplant - equipped with BOF-converters, secondary 
metallurgy, vacuum degassing, continuous and ingots casting - and plate mills. 
Complementary to the core business, a "down-stream" manufacturing unit is available as a branch of the 
Heavy Fabrication: it is mainly focused on the supply of slag-pots made out of cast-steel (GS) 
everywhere the emphasis is placed on large buckets in capacity up to 45 m³
(1.575 cu. feet). 
The expertise of CITICIC  arises from its privilege to be both user and manufacturer of slag 
pots. The extensive experience gained in designing and engineering slag-pots is primarily based on the 
pots operating at the own steel plant and secondly on about 3.000 items produced over the 40 last years 
also in co-operation with manufacturers of slag pot carriers and service providers to metallurgical 
industries. 
The Dillinger slag pots are operating worldwide whereverreliable tools are required for the disposal of 
molten or solid slag which arises from metallurgical or chemical processes. 
Heavy Fabrication Division
Product definition 
The product covered here is a load-bearing device whose sole purpose is to collect molten or solid slag 
generated during metallurgical or chemical processes, to retain it during transport and to deposit it at a 
place of disposal. 
Slag pots are crucial items as they are part of a lifting equipment and therefore undergo in terms of 
mechanical design engineering and handling the national safety regulations of the state where they are 
supposed to be operated. The design of the Dillinger slag pots intended to be used within the European 
Community meets the requirements ofthe European Machinery Directive 2006/42/EC: every slag pots is 
supplied with the CE conformity marking. 
Material 
The pots are made out of the cast-steel DICAST, trade name owned by CITICIC for 
castings: this material is similar to the steels A27/A 27M grade 65-35: April 2003, BS 3100 A1/A2: 
January 1991 or GS 20Mn5 to DIN 17182: May 1992. DICAST is a fully killed steel, vacuum-degassed 
and processed to a fine grain size structure with improved properties both in toughness and in elongation. 
  Chemical compositionverified on product 
Elements C  Si  Mn  P  S 
Required  ≤0.23%  ≤0.55%  ≤1.65%  ≤0.025%  ≤0.025% 
Typical 0.17%  0.40%  1.45% 0.015% 0.002% 
  Mechanical propertieschecked at room temperature in the delivery condition i.e. after completion of 
the quality heat treatment from cylindrical cast-on test blocks (60 mm x 250 mm) available on 
every slag pot: both the sample preparation and the testing comply with ASTM A 370-96. 
Properties Rm Reh
 A  KCV ( average of 3 specimens / individual )  Required  ≥450 MPa  ≥240 MPa  ≥20 %  ≥55 J / 39 J 
Typical  490 MPa  280 MPa  30 %  120 J / 85 J 
  Delivery condition: normalised
Note regarding the material selection: due to obvious advantages in terms of service life and maintenance 
cost-efficiency, cast steel has been becoming more significant in the slag pot construction over the last 
years versus both materials, spheroidal cast-iron and lamellar graphite cast-iron. In contrast to other 
materials, cast steel offers excellent repair possibilities as it is well-suited to welding. 
Manufacturing 
Except the supply of the forgings for trunnions and the engineering of the pattern, all further operations 
are carried-out at the in-house foundry plant. 
  Moulding
the castings are manufactured in a workman-like manner as required in the China standard DIN EN 
1599-1: August 1997, ruling the delivery conditions ofcastings. The moulding is individually carried 
out within a modular flask by using a sand preparation based on resin bonding. 
  Trunnions
the trunnions - when any - are preferably cast-in:they are as a rule manufactured from the steel 
material S355 J2G3 to DIN EN 10250-2: December1999 and forged as per DIN 7527 February 1975. 
Cast-on or hot-fitted trunnions can be also provided. 
  Melting
the melting is carried out in the oxygen steel plant ( 2 off 180 t BOF converters ); the ladle capacity 
allows a continuous bottom pouring process the speed of which is permanently controlled. The metal 
analysis is checked by using a computer linked spectrograph. 
Heavy Fabrication Division
  Heat treatment 
every pot undergoes a combined quality heat treatment (annealing) aiming both to grain refining and 
to stress relieving i.e.: 
- heating to a temperature above AR3, austenitising at about 915°C and controlled cooling in furnace 
- intermediate holding at 600°C - 630°C and completion of cooling in furnace down to 300°C 
  Fettling and dressing
The inner surface is processed fit-for-purpose so that the surface discontinuities - which might cause 
some sticking of the slag - are extensively removed. Additionally, the castings are descaled by shotblasting and the outside is additionally coated for transportation. 
The surface quality results from the comprehensive practice of the manufacturer qualified by the 
requirements of MSS SP-55-1996 (Visual Method for Evaluation of Surface Irregularities). 
Quality assurance
The fabrication route is governed by the provisions of the implemented Quality System ISO 9001: 2000. 
The standard documentation ensures the full traceability of every process step: 
  Manufacturer test certificates according to DIN EN 10.204 § 3.1 including chemical composition, 
mechanical properties and non-destructive examination;
  Dimensional check supported with a "as-built" sketch; 
  Record of the quality heat treatment; 
  Documentation required by the Machinery Directive 2006/42/EC (when applicable). 
Design 
The slag pots can either be manufactured in accordance with a well-tried and proven concept provided by 
the commissioner or be customised to the specific requirements resulting from the operational 
environment. The range of the available design reaches from conventional to most advanced buckets. 
Slag pots are wearing products exposed to both mechanical and alternate thermal stresses the extent of 
them depends on the service conditions. An accurate design aims to minimise the impair of the operative 
environment on the service life: however, it remains always a compromise taking into consideration both 
physical and economical aspects, resulting in a variety of shapes tailored to the site operations. 
A comprehensive data bank resulting from the previous experiences combined with a proper software 
implementing the Finite Element Analysis serves the individual design optimisation. 
Service philosophy 
The marketing strategy of LYHMC  is to enjoy the direct contact to the slag pot operators 
and to establish a long-terms relationship for mutual profit. 
Slag pots are more than just disposable products: we endeavour to propose options in terms of design 
engineering in taking advantage of our double experience as manufacturer and user, always targeting the 
optimisation of their service life. 
Skill with slag pots 
Further information on delivery programme as well as useful advises on product, design, material and 
application are provided by the customer service team of the foundry department: it will support you 
actively in helping you to elaborate the right solution.
Send your message to this supplier
Avatar
Ms. Nicole Shao
*From:
To: Ms. Nicole Shao
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now